Reference standard: EN 12591:2009
| Property |
Unit |
Method |
PARAFALT
ASF 20/30
|
PARAFALT
ASF 30/45
|
PARAFALT
ASF 35/50
|
|---|
| Penetration at 25°C |
0,1 mm |
EN 1426 |
20-30 |
30-45 |
35-50 |
| Softening Point R&B |
ºC |
EN 1427 |
55-63 |
52-60 |
50-58 |
| Retained penetration at 25°C |
% |
EN 12607-1
EN 1426 |
≥ 55 |
≥ 53 |
≥ 53 |
| Increasing of Softening Point R&B |
ºC |
EN 12607-1
EN 1427 |
≤ 10 |
≤ 11 |
≤ 11 |
| Mass change after RTFOT |
% |
EN 12607-1 |
≤ 0,5 |
≤ 0,5 |
≤ 0,5 |
| Flash point, COC |
ºC |
EN ISO 2592 |
≥ 240 |
≥ 240 |
≥ 240 |
| Solubility |
% |
EN 12592 |
≥ 99,0 |
≥ 99,0 |
≥ 99,0 |
| Fraass breaking point |
ºC |
EN 12593 |
- |
≤ -5 |
≤ -5 |
| Properties |
Unit |
Method |
PARAFALT
ASF 50/70
|
PARAFALT
ASF 70/100
|
PARAFALT
ASF 100/150
|
|---|
| Penetration at 25°C |
0,1 mm |
EN 1426 |
50-70 |
70-100 |
100-150 |
| Softening Point R&B |
ºC |
EN 1427 |
46-54 |
43-51 |
39-47 |
| Retained penetration at 25°C |
% |
EN 12607-1
EN 1426 |
≥ 50 |
≥ 46 |
≥ 43 |
| Increasing of Softening Point R&B |
ºC |
EN 12607-1
EN 1427 |
≤ 11 |
≤ 11 |
≤ 12 |
| Mass change after RTFOT |
% |
EN 12607-1 |
≤ 0,5 |
≤ 0,8 |
≤ 0,8 |
| Flash point, COC |
ºC |
EN ISO 2592 |
≥ 230 |
≥ 230 |
≥ 230 |
| Solubility |
% |
EN 12592 |
≥ 99,0 |
≥ 99,0 |
≥ 99,0 |
| Fraass breaking point |
ºC |
EN 12593 |
≤ -8 |
≤ -10 |
≤ -12 |
| Properties |
Unit |
Method |
PARAFALT
ASF 160/220
|
|---|
| Penetration at 25°C |
0,1 mm |
EN 1426 |
160-220 |
| Softening Point R&B |
ºC |
EN 1427 |
35-43 |
| Retained penetration at 25°C |
% |
EN 12607-1
EN 1426 |
≥ 37 |
| Increasing of Softening Point R&B |
ºC |
EN 12607-1
EN 1427 |
≤ 12 |
| Mass change after RTFOT |
% |
EN 12607-1 |
≤ 1,0 |
| Flash point, COC |
ºC |
EN ISO 2592 |
≥ 220 |
| Solubility |
% |
EN 12592 |
≥ 99,0 |
| Fraass breaking point |
ºC |
EN 12593 |
≤ -15 |